Several CeO(2)-based mixed oxides with general composition Ce(1-x)Ln(x)O(2-x/2) (for 0 ≤ x ≤ 1 and Ln = La, Nd, Sm, Eu, Gd, Dy, Er, or Yb) were prepared using an initial oxalic precipitation leading to a homogeneous distribution of cations in the oxides. After characterization of the Ce/Nd oxalate precursors and then thermal conversion to oxides at T = 1000 °C, investigation of the crystalline structure of these oxides was carried out by XRD and μ-Raman spectroscopy. Typical fluorite Fm ̅3m structure was obtained for relatively low Ln(III) contents, while a cubic Ia ̅3̅ superstructure was evidenced above x ≈ 0.4. Moreover, since Nd(2)O(3) does not crystallize with the Ia ̅3̅-type structure, two-phase systems composed with additional hexagonal Nd(2)O(3) were obtained for x(Nd) ≥ 0.73 in the Ce(1-x)Nd(x)O(2-x/2) series. The effect of heat treatment temperature on these limits was explored through μ-Raman spectroscopy, which allowed determining the presence of small amounts of the different crystal structures observed. In addition, the variation of the Ce(1-x)Ln(x)O(2-x/2) unit cell parameter was found to follow a quadratic relation as a result of the combination between increasing cationic radius, modifications of cation coordination, and decreasing O-O repulsion caused by oxygen vacancies.
© 2011 American Chemical Society