Hybrid polyelectrolyte multilayer systems were fabricated on top of planar surfaces and colloidal particles via layer by layer (LbL) assembly of polystyrene sulphonate (PSS) and polybenzyl methacrylate-block-poly(dimethylamino)ethyl methacrylate (PBzMA-b-PDMAEMA) polymersomes. Polymersomes were prepared by self assembly of PBzMA-b-PDMAEMA copolymer, synthesised by group transfer polymerisation. Polymersomes display a diameter of 270 nm and a shell thickness of 11nm. Assembly on planar surfaces was followed by means of the Quartz Crystal Microbalance with Dissipation (QCM-D) and Atomic Force Microscopy (AFM). Detailed information on the assembly mechanism and surface topology of the polymersome/polyelectrolyte films was thereby obtained. The assembly of polymersomes and PSS on top of silica particles of 500 nm in diameter was confirmed by ζ-potential measurements. Confocal laser scanning microscopy (CLSM), scanning electron microscopy (SEM) and transmission electron microscopy (TEM) revealed that polymersome/PSS coated silica particles increase in total diameter up to 3-5μm. This hints toward the formation of densely packed polymersome layers. In addition, CLSM showed that polymersome/PSS films exhibit a high loading capacity that could potentially be used for encapsulation and delivery of diverse chemical species. These results provide an insight into the formation of multilayered films with compartmentalised hydrophilic/hydrophobic domains and may lead to the successful application of polymersomes in surface-engineered colloidal systems.
Keywords: Colloidal nanomaterials; Layer-by-layer assembly; Polymersomes.
Copyright © 2014 Elsevier Inc. All rights reserved.