We investigated the mechanism(s) of the anomalous Hall effect (AHE) in magnetic granular materials by fabricating 100 nm-thick thin films of Co x (MgO)100-x with a Co volume fraction of 34 ⩽ x ⩽ 100 using co-sputtering at room temperature. We measured the temperature dependence of longitudinal resistivity ([Formula: see text]) and anomalous Hall resistivity ([Formula: see text]) from 5 K to 300 K in all samples. We found that when x decreases from 100 to 34, the values of [Formula: see text] and [Formula: see text] respectively increased by about four and three orders in magnitude. By linearly fitting the data, obtained at 5 K, of anomalous Hall coefficient ([Formula: see text]) and of [Formula: see text] to [Formula: see text], we found that our results perfectly fell on a straight line with a slope of [Formula: see text] 0.97 ± 0.02. This fitting value of [Formula: see text] in [Formula: see text] clearly suggests that skew scattering dominated the AHE in this granular system. To explore the effect of the scattering on the AHE, we performed the same measurements on annealed samples. We found that although both [Formula: see text] and [Formula: see text] significantly reduced after annealing, the correlation between them was almost the same, which was confirmed by the fitted value, [Formula: see text] = 0.99 ± 0.03. These data strongly suggest that the AHE originates from the skew scattering in Co-MgO granular thin films no matter how strong the scattering of electrons by the interfaces and defects is. This observation may be of importance to the development of spintronic devices based on MgO.