Synthesis of zeolite membranes on calcium silicate support and their bioactive response

Prog Biomater. 2018 Mar;7(1):61-71. doi: 10.1007/s40204-018-0085-2. Epub 2018 Feb 10.

Abstract

The synthesis of calcium silicate supported zeolite membrane was carried out by second growth method. The chemical nature of the functionalizing agent on the formation of homogenous zeolite membrane was evaluated. One monomer and two cationic polymers were used: 3-aminopropyltriethoxysilane (APS), polyethylenimine (PEI) and polydiallyldimethylammonium chloride (PDDA). The support was subjected to chemical functionalization and then it was rubbed with zeolite crystals. The W zeolite was used as zeolite seed in two different Si/Al ratios. The functionalized and rubbed supports were submitted to hydrothermal treatment at 150 °C for 48 h. The bioactivity of the homogeneous zeolite membranes was evaluated by the biomimetic method through the membranes soaking in a simulated body fluid (SBF) at 37 °C for 21 days. Two immersion methods were evaluated. The products were characterized by XRD and SEM techniques. The results indicated that the supported functionalization with PDDA and the Si/Al ratio (higher than 1.8) of zeolite enhanced the interaction between the support and the zeolite precursor enhancing the formation of homogeneous zeolite membrane on the surface. The presence of the functional groups of PDDA on the membrane was detected by FTIR. After immersion in SBF, the zeolite membrane was stable and led to the formation of Ca-P layer on its surface. The re-immersion method led to the formation of richer Ca/P layer (1.36). These findings allowed generating a zeolite membrane with combined properties of calcium silicate and the controllable porosity of zeolitic material making it potentially useful for bone regeneration and drug releasing.

Keywords: Bioactivity; Calcium silicate; Cationic polymer; Membrane; Second growth; Zeolite.

Grants and funding