Template Engineering of CuBi2 O4 Single-Crystal Thin Film Photocathodes

Abstract

To develop strategies for efficient photo-electrochemical water-splitting, it is important to understand the fundamental properties of oxide photoelectrodes by synthesizing and investigating their single-crystal thin films. However, it is challenging to synthesize high-quality single-crystal thin films from copper-based oxide photoelectrodes due to the occurrence of significant defects such as copper or oxygen vacancies and grains. Here, the CuBi₂ O₄ (CBO) single-crystal thin film photocathode is achieved using a NiO template layer grown on single-crystal SrTiO₃ (STO) (001) substrate via pulsed laser deposition. The NiO template layer plays a role as a buffer layer of large lattice mismatch between CBO and STO (001) substrate through domain-matching epitaxy, and forms a type-II band alignment with CBO, which prohibits the transfer of photogenerated electrons toward bottom electrode. The photocurrent densities of the CBO single-crystal thin film photocathode demonstrate -0.4 and -0.7 mA cm^-2 at even 0 V_RHE with no severe dark current under illumination in a 0.1 m potassium phosphate buffer solution without and with H₂ O₂ as an electron scavenger, respectively. The successful synthesis of high-quality CBO single-crystal thin film would be a cornerstone for the in-depth understanding of the fundamental properties of CBO toward efficient photo-electrochemical water-splitting.

Keywords: CuBi 2O 4; single-crystal thin films; template engineering.