This in vitro study evaluated the influence of feldspathic ceramic thickness on the properties of light- and dual-cured resin cements. For each cement (RelyX Veneer, Allcem Veneer, RelyX Ultimate, and Allcem Dual), three ceramic specimens were prepared, with seven thicknesses for each (0.5, 1.0, 1.5, 2.0, 2.5, 3.0, and 3.5 mm). The degree of conversion, Vickers microhardness, irradiance power, color variation (ΔE00 ), and translucency parameters were assessed. Microhardness and irradiance power were analyzed using analysis of variance (ANOVA) with post hoc Tukey's test, while ΔE00 , translucency parameters, and degree of conversion were analyzed using ANOVA of ranks with post hoc Duncan's Multiple Range Test. The relationship between each of the dependent variables (degree of conversion, ΔE00 , and translucency parameter tests) and the specimen thickness was described using linear regression for each of the four resin cements. The significance level for all analyses was set at 5%. RelyX Ultimate yielded the lowest degree of conversion values among all resin cements. Allcem Veneer produced the lowest microhardness values, without statistical differences between thicknesses, of up to 1 mm. Allcem Dual produced the highest ΔE00 and translucency parameter values. Feldspathic ceramic thickness influenced the mechanical properties of resin cements and optical aspects of the restorative set.
Keywords: ceramics; in vitro techniques; polymerization; resin cement; spectrophotometry.
© 2021 European Journal of Oral Sciences.