Annealing of Al-Zn-Mg-Cu Alloy at High Pressures: Evolution of Microstructure and the Corrosion Behavior

Materials (Basel). 2021 Apr 20;14(8):2076. doi: 10.3390/ma14082076.

Abstract

Extruded Al-Zn-Mg-Cu alloy samples with grains aligned parallel to the extrusion direction were subjected to high-pressure annealing. The effects of annealing pressure on the microstructure, hardness, and corrosion properties (evaluated using potentiodynamic polarization (PDP) and electrochemical impedance spectroscopy (EIS)) were investigated. Phase analysis showed the presence of MgZn2 and α-Al phases, the MgZn2 phase dissolved into the matrix, and its amount decreased with the increasing annealing pressure. The recrystallization was inhibited, and the grains were refined, leading to an increase in the Vickers hardness with increasing the annealing pressure. The corrosion resistance was improved after high-pressure treatment, and a stable passivation layer was observed. Meanwhile, the number of corrosion pits and the width of corrosion cracks decreased in the high-pressure annealed samples.

Keywords: Al-Zn-Mg-Cu alloy; corrosion behavior; high-pressure annealing; microstructure.