By introducing thiourea and ether groups into MQ silicone resin polymer via free radical polymerization, a polyether-thiourea-siloxane (PTS) copolymer was synthesized. The characterization of the synthesized copolymer indicated the occurrence of H-bonding interactions and a narrow molecular weight polydispersity index. Antifouling coatings were produced by incorporating the synthesized copolymer and phenylmethylsilicone oil (PSO). The addition of a minute amount of copolymer enhanced the hydrophobicity of the coating by increasing its surface roughness. However, excessive addition of copolymer resulted in a significant deterioration of the coating surface smoothness. The copolymer improved the mechanical properties of the coating, but excessive addition decreased the crosslinking density and weakened the mechanical performance. With increasing copolymer addition, the leaching of PSO was significantly improved due to the change in the storage form of PSO in the coating caused by the copolymer. Based on the H-bonding interaction of the copolymer, the adhesion strength between the coating and the substrate was significantly improved. However, excessive addition of copolymer did not infinitely enhance the adhesion strength. The antifouling performance demonstrated that an appropriate amount of copolymer could obtain adequate PSO leaching efficiency, thereby effectively enhancing the antifouling performance of the coating. In this study, the prepared coating P12 (12 g of PTS in 100 g of PDMS) showed the most effective antifouling performance.
Keywords: H-bonding interaction; copolymer; fouling release; leaching; marine antifouling.