Investigation of iron oxide shell and iron core in magnetically-assisted synthetized wire-like nanochains

Abstract

The zerovalent iron (Fe⁰) nanomaterials tend to be spontaneously oxidized in the presence of oxygen. This leads to the formation of interface composed of iron core and thin iron oxide shell. These structures are frequently observed with transmission electron microscope but, at the same time, it is hard to determine the precise structural and chemical composition of oxide shell. This feature is very important for possible applications of Fe⁰nanostructures. Hence, the present work aims to deliver more detailed insights in this topic. The investigations are performed for the iron nanochains prepared in the magnetic-field-induce reduction of FeCl₃by NaBH₄. The high-resolution transmission electron microscopy, electron energy loss spectroscopy, and x-ray photoemission spectroscopy confirm that the iron nanochains are covered by very thin oxide layer not exceeding over 3 nm. Moreover, the detailed XPS analyses of O 1s and Fe 2p lines indicate that the iron oxide shell reveals Fe₃O₄nature. Moreover, this work demonstrated that some by-products of the reaction containing boron are presented in the sample even after a removal of the thin iron oxide shell by Ar⁺treatment.

Keywords: iron nanochains; magnetic-field-induced synthesis; surface oxidation; x-ray photoemission spectroscopy.