Applying microelectrodes to investigate aged ductile iron and copper coupon reactivity during free chlorine application

Abstract

In drinking water distribution systems, including premise plumbing, dissolved oxygen (DO) and free chlorine (FC) are common oxidants and ductile iron (DI) and copper (Cu) are commonly used pipe materials. Microelectrodes as a tool have been applied in previous corrosion research and were used in this study to collect quantifiable data and understand DO and FC reactivity and pH changes at the water-metal interface. Using microelectrodes, pH, DO, and FC profiles from the bulk water to near and at the surface of aged DI (154-190 d) and Cu (2 d and 86-156 d) coupons were investigated during periods of flow and stagnation (30 min). Using the measured microelectrode profiles, oxidant fluxes and apparent surface reaction rate constants were calculated to elucidate differences between DO and FC reactivity with the coupons. Microelectrodes were successfully applied to measure pH, DO, and FC profiles from the bulk water to near aged DI and Cu coupon surfaces; Cu coupons aged quickly and exhibited less reactivity at 2 d with DO and FC than aged DI coupons did after 154-190 d; and for the aged DI coupon experiments, orthophosphate presence stabilized pH profiles where without orthophosphate pH fluctuations of greater than 2 pH units occurred from the bulk water to the DI coupon surface.

Keywords: Copper; Corrosion; Ductile iron; Free chlorine; Microelectrode; Orthophosphate.