Silica aerogels exhibit exceptional characteristics such as mesoporosity, light weight, high surface area, and pore volume. Nevertheless, their utilization in industrial settings remains constrained due to their brittleness, moisture sensitivity, and costly synthesis procedure. Several studies have proved that adding nanofillers, such as carbon nanotubes (CNT) or graphene nanoplatelets (GNP), can improve the mechanical strength of the aerogels. The incorporation of nanofillers is often accompanied by agglomeration and pore blockage, which, in turn, deteriorates the surface area, pore volume, and low density. Including flexible melamine foam (MF) as a scaffold for the silica aerogel and nanofiller composite can prevent the restacking of the nanofillers through π-π interaction, hence maintaining the incredible properties of aerogels and improving their mechanical properties. CNT, GNP, and the polymeric silica precursor, polyvinyltrimethoxysilane (PVTMS), were added to a MF, at varying concentrations, to fabricate the MF-aerogel nanocomposites. Surfactant and sonication were utilized to ensure a homogeneous dispersion of the nanofillers in the system. The presence of MF prevented the agglomeration of nanofillers, resulting in lower density and relatively higher surface properties (SBET up to 929 m2·g-1 and pore volume up to 4.34 cc·g-1). Moreover, the MF-supported samples could endure 80% strain without breakage and showed an outstanding compressive strength of up to ∼20 MPa. These aerogel nanocomposites also demonstrated an excellent volatile organic compound (∼2680 mg·g-1) and cationic dye adsorption (∼10 mg·g-1).
Keywords: CNT; GNP; PVTMS; VOC adsorption; melamine foam; silica aerogel.