This paper presents a study on the combined use of two by-products, namely quarry dust (QD) and ferronickel slag (FNS), as a full substitute for natural sand to improve the greenness of concrete production. Quarry dust was used in increments of 25% to a maximum of 75% substitution, where nickel slag was used as the remaining proportion of fine aggregate. All the combinations of quarry dust and nickel slag were found to be compliant with AS 2758.1 and they showed notably better grading than 100% sand. In this research, standard concrete tests, such as the slump test for fresh concrete, and compression, tensile and shrinkage tests for hardened concrete, were conducted. Scanning electron microscopy and X-ray diffraction analysis were also conducted for microstructural investigation. The results concluded that the combinations of quarry dust and nickel slag in concrete as a whole substitution of sand provide similar results for these properties. Specifically, 25% quarry dust with 75% nickel slag proved to be the most promising alternative to sand, with compressive and splitting tensile strengths of 62 and 4.29 MPa, respectively, which were 16% and 20% higher than those of the control mix. Also, lower drying shrinkage was observed for this combination compared to the control mix. The higher strength is attributed to the rough texture and angular shape of both quarry dust and nickel slag providing a better mechanical interlocking. The validity of this result has also been confirmed through image analysis of micrographs from various specimens. In microstructural investigations, specimens with QD and FNS exhibited fewer voids and a more compact surface compared to the control specimen. This shows the potential for further research into the use of quarry dust and nickel slag in the production of green concrete.
Keywords: ferronickel slag; mechanical properties; microstructure; quarry dust.