This study focuses on the calcined coal gangue (CCG)-blended cements containing Stöber nano-SiO2 (SNS) particles. The effects of SNS particles on the workability, hydration behaviour, mechanical properties and microstructure evolution of the blended cements were comprehensively investigated at curing ages ranging from 1 to 28 d. The hydration behaviour was studied via isothermal calorimetry test, X-ray diffraction (XRD) and thermogravimetric (TG) tests. The microstructural evolution was studied using mercury intrusion porosimetry (MIP) and scanning electron microscopy (SEM). The results show that the incorporation of SNS led to a significant reduction in fluidity, particularly at an SNS content of 3%. The SNS significantly increased the compressive strength of the CCG-blended cement at all curing ages, and the optimum SNS content was found to be 2%. SNS significantly accelerated not only the early cement hydration but also the pozzolanic reaction of CCG at later curing ages, resulting in a decrease in portlandite, as evidenced by the isothermal calorimetry, XRD and TG analysis. Microstructural analysis shows that the incorporation of SNS effectively refined the pore structure of the CCG-blended cement, resulting in the formation of a dense microstructure. All these beneficial effects of SNS provides advantages in the development of the compressive strength of the CCG-blended cement at all curing ages.
Keywords: Stöber nano-SiO2; calcined coal gangue; cement; compressive strength; hydration.