High-performance wearable microsupercapacitor (MSC) as energy storage components is highly desirable for developing self-powering wearable electronics. However, synthesis of MSC electrode film concurrently possessing large area, ultrathin thickness, and high areal energy storage capability is still challenging. Herein, a universal strategy is reported to synthesize large-area and ultrathin metal oxide nanoparticles (MONPs)/reduced graphene oxide (rGO) hybrid-structured films by attaching self-assembled film of a wide range of MONPs onto self-assembled rGO film and subsequent carbonization. Combining a template-assisted patterning strategy and a floating film salvaging process, flexible symmetric and asymmetric MSCs based on MONPs@C/rGO films can be easily prepared in large areas. MONP agglomeration is avoided and its pseudocapacitive behavior is well utilized, thereby realizing a high areal specific capacitance of 9.32 mF cm-2 in Fe3O4@C/rGO-based symmetric MSC at a film thickness of only 275 nm, corresponding to a high volumetric specific capacitance of 338.9 F cm-3. Moreover, the MnO@C/rGO‖Fe3O4@C/rGO-based asymmetric MSC delivers a high volumetric energy density of 69.8 mWh cm-3. The MSCs also demonstrate their efficient power supply in wearable self-powering systems. This work provides a new route for scalable preparation of high-performance wearable MSCs, and also enables customizable fabrication and performance tuning of MSCs.
Keywords: large area; microsupercapacitor; monodispersed metal oxide nanoparticles; ultrathin film; universal strategy.
© 2024 Wiley‐VCH GmbH.